Yaa Methods Of Resin Coating For Fusible Interlining
Tuesday 18 December 2018
Edit
Methods of Resin Coating for Fusible Interlining
Noor Ahmed Raaz
B. Sc inwards Textile Engineer (CU)
Specialized inwards Apparel Manufacturing
Merchandiser, A.M.C.S Textile Ltd (AEPZ)
Email: raju.uttara105@gmail.com
B. Sc inwards Textile Engineer (CU)
Specialized inwards Apparel Manufacturing
Merchandiser, A.M.C.S Textile Ltd (AEPZ)
Email: raju.uttara105@gmail.com
Methods of Resin Coating:
Resin equally a coating stuff is applied on the base of operations stuff past times unlike methods. Methods of resin coating impact the properties of fusible interlining, which are described below:
I. Scatter coating: Resin is sprayed on the base of operations stuff past times a spray head. Then temperature in addition to line per unit of measurement area are used to laid upward the resin on the base of operations fabric. The molecular size of the resin varies betwixt 150 to 400 microns. Properties of interlining is non all through uniform inwards this type of coated interlining, thus this type of interlining is cheaper than others.
II. Dry–dot–coating: Powder of resin is applied on the base of operations stuff inwards point shape past times an engraved roller, so the base of operations stuff is passed through an oven, where due to temperature the resin melts in addition to due to line per unit of measurement area of roller the resin sticks on the base of operations fabric. Number of dots per cm may hold upward iii to 12 in addition to size of resin particles vary from lxxx to 200 microns. For fine stuff finer dots in addition to for coarser stuff larger dots are used. Property of this type of interlining is all through uniform.
III. Paste interlining: Resin pulverization is converted into glue past times the piece of occupation of chemicals in addition to water. Then the glue is printed on the base of operations fabric. Then past times applying temperature H2O in addition to chemicals are evaporated from the base of operations fabric. Very fine dots are produced past times printing technique amongst resin size 1 to lxxx microns. Property is all through uniform.
IV. Film coating: Resin is get-go melted past times the piece of occupation of temperature in addition to so applied on the base of operations stuff equally a really fine cinema on 1 side of the fabric. Polyethylene equally a resin is used for cinema coating. Flexibility of cinema coated interlining is quite less than others.
V. Emulsion coating: Resin is made equally emulsion shape amongst the piece of occupation of chemicals in addition to water. Then through this emulsion base of operations stuff is passed which picks upward emulsion. By the piece of occupation of a mash roller emulsion accept upward is controlled. Then the stuff is passed through an oven where the interlining is dried. This type of interlining is really difficult later fusing.
I. Scatter coating: Resin is sprayed on the base of operations stuff past times a spray head. Then temperature in addition to line per unit of measurement area are used to laid upward the resin on the base of operations fabric. The molecular size of the resin varies betwixt 150 to 400 microns. Properties of interlining is non all through uniform inwards this type of coated interlining, thus this type of interlining is cheaper than others.
II. Dry–dot–coating: Powder of resin is applied on the base of operations stuff inwards point shape past times an engraved roller, so the base of operations stuff is passed through an oven, where due to temperature the resin melts in addition to due to line per unit of measurement area of roller the resin sticks on the base of operations fabric. Number of dots per cm may hold upward iii to 12 in addition to size of resin particles vary from lxxx to 200 microns. For fine stuff finer dots in addition to for coarser stuff larger dots are used. Property of this type of interlining is all through uniform.
 |
| Fusible interlining |
IV. Film coating: Resin is get-go melted past times the piece of occupation of temperature in addition to so applied on the base of operations stuff equally a really fine cinema on 1 side of the fabric. Polyethylene equally a resin is used for cinema coating. Flexibility of cinema coated interlining is quite less than others.
V. Emulsion coating: Resin is made equally emulsion shape amongst the piece of occupation of chemicals in addition to water. Then through this emulsion base of operations stuff is passed which picks upward emulsion. By the piece of occupation of a mash roller emulsion accept upward is controlled. Then the stuff is passed through an oven where the interlining is dried. This type of interlining is really difficult later fusing.